Publicación: Mechanochemical Synthesis and Nitrogenation of the Nd1.1Fe10CoTi Alloy for Permanent Magnet
dc.contributor.author | Martínez Sánchez, Hugo | |
dc.contributor.author | Hadjipanayis, George | |
dc.contributor.author | Pérez Alcázar, Germán Antonio | |
dc.contributor.author | Zamora Alfonso, Ligia Edith | |
dc.contributor.author | Trujillo Hernández, Juan Sebastián | |
dc.date.accessioned | 2021-11-12T22:02:42Z | |
dc.date.available | 2021-11-12T22:02:42Z | |
dc.date.issued | 2021-06-24 | |
dc.description.abstract | In this work, the mechanochemical synthesis method was used for the first time to produce powders of the nanocrystalline Nd1.1Fe10CoTi compound from Nd2O3, Fe2O3, Co and TiO2. High-energy-milled powders were heat treated at 1000 °C for 10 min to obtain the ThMn12-type structure. Volume fraction of the 1:12 phase was found to be as high as 95.7% with 4.3% of a bcc phase also present. The nitrogenation process of the sample was carried out at 350 °C during 3, 6, 9 and 12 h using a static pressure of 80 kPa of N2. The magnetic properties Mr, µ0Hc, and (BH)max were enhanced after nitrogenation, despite finding some residual nitrogen-free 1:12 phase. The magnetic values of a nitrogenated sample after 3 h were Mr = 75 Am2 kg–1, µ0Hc = 0.500 T and (BH)max = 58 kJ·m–3. Samples were aligned under an applied field of 2 T after washing and were measured in a direction parallel to the applied field. The best value of (BH)max ~ 114 kJ·m–3 was obtained for 3 h and the highest µ0Hc = 0.518 T for 6 h nitrogenation. SEM characterization revealed that the particles have a mean particle size around 360 nm and a rounded shape. | es_CO |
dc.description.sponsorship | Universidad de Ibagué | es_CO |
dc.identifier.citation | Martínez Sánchez, H.; Hadjipanayis, G.; Pérez Alcázar, G.A.; Zamora Alfonso, L.E.; Trujillo Hernández, J.S. Mechanochemical Synthesis and Nitrogenation of the Nd1.1Fe10CoTi Alloy for Permanent Magnet. Molecules 2021, 26, 3854. https://doi.org/10.3390/molecules26133854 | es_CO |
dc.identifier.issn | 1420-3049 | |
dc.identifier.uri | https://www.mdpi.com/1420-3049/26/13/3854 | |
dc.language.iso | en | es_CO |
dc.publisher | Molecules | es_CO |
dc.subject | Permanent magnets | es_CO |
dc.subject | Mechanochemical synthesis | es_CO |
dc.subject | Nitrogenation | es_CO |
dc.subject | Extrinsic magnetic properties | es_CO |
dc.subject | X-ray diffraction patterns | es_CO |
dc.subject | Spin reorientation | es_CO |
dc.title | Mechanochemical Synthesis and Nitrogenation of the Nd1.1Fe10CoTi Alloy for Permanent Magnet | es_CO |
dc.type | Article | es_CO |
dspace.entity.type | Publication | |
eperson.email | juan.trujillo@unibague.edu.co | es_CO |
Archivos
Bloque de licencias
1 - 1 de 1
Cargando...
- Nombre:
- license.txt
- Tamaño:
- 134 B
- Formato:
- Item-specific license agreed upon to submission
- Descripción: